Compound 7017 Data Sheet
60-duro EPM
| ASTM Method |
Property |
Avg. Value |
Min. Value |
| D412 Method A |
Tensile Strength |
2118 psi |
1531 psi |
|
Ultimate Elongation |
551% |
232% |
|
Stress at Elongation |
|
|
|
- M25 |
138 psi |
|
|
- M50 |
178 psi |
131 psi |
|
- M100 |
248 psi |
145 psi |
|
Strain Energy/ Unit
Volume at 20% elongation |
17 psi |
|
|
Calculated Shear Modulus,
G |
312 psi |
|
|
Calculated Youngs
Modulus, E |
935 psi |
|
|
E-secant from the initial
slope |
879 psi |
|
| D624, Die B |
Tear Strength |
|
|
| D297, 15 |
Specific Gravity |
|
|
| |
|
Max Value |
Min Value |
| D2240, Type A |
Durometer Hardness |
62 points |
57 points |
| |
|
|
|
| D395, Test B |
Compression Set |
Avg. Value |
|
|
22 hrs @ F |
|
|
|
70 hrs @ F |
|
|
|
336 hrs @ F |
|
|
ASTM D865 - Dry Heat Aging:
| Hours Aged |
Change in Tensile |
Change in Elongation |
Change in Durometer |
| 70 hrs @ F |
|
|
|
| 168 hrs @ F |
|
|
|
| 336 hrs @ F |
|
|
|
| 1000 hrs @ F |
|
|
|
Temperature Properties and Shelf Life:
| ASTM / Other |
Description |
Value |
| D746 |
Brittle Point |
|
| D1329 |
Temp Retraction TR-10 |
|
| |
Glass Transition |
-60F |
| |
Max Operating Temp |
|
| |
Shelf Life (years) |
|
Rev. 8/30/1995