Compound 5795 Data Sheet
90-duro FKM
ASTM Method |
Property |
Avg. Value |
Min. Value |
D412 Method A |
Tensile Strength |
1996 psi |
1784 psi |
|
Ultimate Elongation |
94% |
85% |
|
Stress at Elongation |
|
|
|
- M25 |
834 psi |
|
|
- M50 |
1217 psi |
1174 psi |
|
- M100 |
|
|
|
Strain Energy/ Unit
Volume at 20% elongation |
110 psi |
|
|
Calculated Shear Modulus,
G |
2053 psi |
|
|
Calculated Youngs
Modulus, E |
6160 psi |
|
|
E-secant from the initial
slope |
5713 psi |
|
D624, Die B |
Tear Strength |
201 lbf/inch |
|
D297, 15 |
Specific Gravity |
1.88 |
|
|
|
Max Value |
Min Value |
D2240, Type A |
Durometer Hardness |
93 points |
87 points |
|
|
|
|
D395, Test B |
Compression Set |
Avg. Value |
|
|
22 hrs @ 392F |
20% |
|
|
70 hrs @ 392F |
24% |
|
|
336 hrs @ 392F |
37% |
|
ASTM D865 - Dry Heat Aging:
Hours Aged |
Change in Tensile |
Change in Elongation |
Change in Durometer |
70 hrs @ 392F |
12% |
14% |
0 points |
168 hrs @ 392F |
11% |
16% |
1 points |
336 hrs @ 392F |
19% |
9% |
1 points |
1000 hrs @ 392F |
|
|
|
Temperature Properties and Shelf Life:
ASTM / Other |
Description |
Value |
D746 |
Brittle Point |
|
D1329 |
Temp Retraction TR-10 |
-24F |
|
Glass Transition |
-14F |
|
Max Operating Temp |
400F |
|
Shelf Life (years) |
20 |
Rev. 4/18/2011